Technical data sheets
Download SK Functional Polymer brochures and technical data sheets
Lotryl® Bestpeel range
The data displayed in the tables below are typical values but should not be considered as commercial specifications.
| Specified properties* | Typical properties | ||||
| Grades | Technical Datasheet |
Acrylate content
(%) |
Melt index (g/10min) |
Melting point (C°) |
Density (g/cm3) |
| Bestpeel 2008 (New) |  |
- | 7 | 79 | 1.05 |
| Bestpeel 2012 | |
20 | 11 | 79 | 0.95 |
| Bestpeel 2407 | |
22-25 | 1-3 | 72 | 0.94 |
| Test method | FTIR |
|
D.S.C. |
|
|
| ISO standard | SK Functional Polymer | ISO 1133 |
ISO 11357-3 |
ISO 1183 |
|
Melt Index: 190°C, 2.16kg
*Properties routinely measured during the standard quality control procedure.
Lotryl® T range
The data displayed in the tables below are typical values but should not be considered as commercial specifications.
| Specified properties* | Typical properties | |||||||||||
| Grades | Technical Datasheet |
Acrylate content
(%) |
Melt index (g/10min) |
Melting point (C°) |
Vicat T° (C°) |
Ring and ball T° (C°) |
Tensile strength
at break (MPa) |
Elonga- tion at break (%) |
Flex.
Modul. (MPa) |
Hard- ness Shore A |
Hard- ness Shore D |
Density (g/cm3) |
| 24MA02T | |
23-26 | 1-3 | 96 | 40 | - | 12 | 800 | 17 | 81 | 24 | 0.95 |
| 24MA07T | |
23-26 | 6-8 | 98 | 40 | 0.95 | ||||||
| 29MA03T | |
27-31 | 2-3.5 | 92 | <40 | - | 12 | 900 | 12 | 73 | 18 | 0.95 |
| 28BA175T | |
26-30 | 150-200 | 97 | <40 | 109 | - | - | <10 | - | - | 0.94 |
| 28BA700T / HMA-LV | |
26-30 | 600-800 | 94 | <40 | 100 | - | - | - | - | - | 0.93 |
| 35BA40T | |
33-37 | 35-45 | 89 | <40 | 134 | 1.8 | 400 | <10 | 60 | - | 0.93 |
| 35BA320T / HMA | |
33-37 | 260-350 | 90 | <40 | 102 | 1.3 | 110 | <10 | 54 | - | 0.93 |
|
Test method |
FTIR |
ASTM D1238 |
D.S.C. |
ASTM D1525 |
ASTM E28 |
ASTM D638 |
ASTM D638 |
ASTM D 638 |
ASTM D790 |
ASTM D2240 |
ASTM D792 |
|
| ISO standard | SK Functional Polymer | ISO 1133 | ISO 11357-3 |
ISO 306 | ISO 527-2 | ISO 527-2 | ISO 527-2 | ISO 868 | ISO 868 | ISO 1183 | ||
Melt Index: 190°C, 2.16kg
*Properties routinely measured during the standard quality control procedure.
Lotryl® range
The data displayed in the tables below are typical values but should not be considered as commercial specifications.
| Specified properties* | Typical properties | |||||||||||
| Grades | Technical Datasheet |
Acrylate content
(%) |
Melt index (g/10min) |
Melting point (C°) |
Vicat T° (C°) |
Ring and ball T° (C°) |
Tensile strength
at break (MPa) |
Elonga- tion at break (%) |
Flex.
Modul. (MPa) |
Hard- ness Shore A |
Hard- ness Shore D |
Density (g/cm3) |
| 17BA04 | |
16-19 | 3.5-4.5 | 93 | 60 | - | 15 | 700 | 45 | - | 32 | 0.93 |
| 28BA175 | |
26-30 | 150-200 | 80 | 40 | 94 | 3 | 300 | 23 | 80 | - | 0.93 |
| 30BA02 | |
27-32 | 1.5-2.5 | 78 | 41 | >190 | 6 | 850 | 9 | 75 | - | 0.93 |
| 35BA40 | |
33-37 | 35-45 | 66 | <40 | 110 | 2 | 600 | - | 70 | - | 0.93 |
| 35BA320 | |
33-37 | 260-350 | 65 | <40 | 85 | 1.5 | 200 | - | 52 | - | 0.93 |
| 18MA02 | |
17-20 | 2-3 | 83 | 53 | - | 13 | 700 | 50 | - | 25 | 0.94 |
| 20MA08 | |
19-21 | 7-9 | 80 | 46 | - | 9 | 800 | 20 | 83 | - | 0.94 |
| 24MA005 | |
23-26 | 0.4-0.7 | 72 | 45 | - | 17 | 750 | 18 | 84 | - | 0.94 |
| 24MA02 | |
23-26 | 1-3 | 68 | <40 | - | 9 | 800 | 12 | 79 | 22 | 0.94 |
| 28MA07 | |
26-30 | 6-8 | 65 | <40 | 7 | 900 | 10 | 76 | - | 0.95 | |
| 29MA03 | |
27-31 | 2.0-3.5 | 61 | <40 | 175 | 6 | 900 | <10 | 75 | - | 0.95 |
| Test method |
FTIR |
ASTM D1238 |
D.S.C. |
ASTM D1525 |
ASTM E28 |
ASTM D638 |
ASTM D790 |
ASTM D2240 |
ASTM D792 |
|||
| ISO standard | SK Functional Polymer | ISO 1133 |
ISO 11357-3 |
ISO 306 |
- | ISO R 527 |
ISO 178 |
ISO 868 |
ISO 1183 |
|||
Melt Index: 190°C, 2.16kg
*Properties routinely measured during the standard quality control procedure.